Synthesis, structure and optical properties of the laser synthesized Al2O3 nanopowders depending on the crystallite size and vaporization atmosphere. / Kostyukov, Anton I.; Snytnikov, Valeriy N.; Yelisseyev, Alexander P. et al.

In: Advanced Powder Technology, Vol. 32, No. 8, 08.2021, p. 2733-2742.

Research output: Contribution to journal › Article › peer-review

Harvard

Kostyukov, AI, Snytnikov, VN, Yelisseyev, AP, Zhuzhgov, AV, Kostyukova, NY, Ishchenko, AV, Cherepanova, SV & Snytnikov, VN 2021, 'Synthesis, structure and optical properties of the laser synthesized Al2O3 nanopowders depending on the crystallite size and vaporization atmosphere', Advanced Powder Technology, vol. 32, no. 8, pp. 2733-2742. https://doi.org/10.1016/j.apt.2021.05.044

APA

Kostyukov, A. I., Snytnikov, V. N., Yelisseyev, A. P., Zhuzhgov, A. V., Kostyukova, N. Y., Ishchenko, A. V., Cherepanova, S. V., & Snytnikov, V. N. (2021). Synthesis, structure and optical properties of the laser synthesized Al2O3 nanopowders depending on the crystallite size and vaporization atmosphere. Advanced Powder Technology, 32(8), 2733-2742. https://doi.org/10.1016/j.apt.2021.05.044

Vancouver

Kostyukov AI, Snytnikov VN, Yelisseyev AP, Zhuzhgov AV, Kostyukova NY, Ishchenko AV et al. Synthesis, structure and optical properties of the laser synthesized Al2O3 nanopowders depending on the crystallite size and vaporization atmosphere. Advanced Powder Technology. 2021 Aug;32(8):2733-2742. Epub 2021 Jun 4. doi: 10.1016/j.apt.2021.05.044

Author

Kostyukov, Anton I. ; Snytnikov, Valeriy N. ; Yelisseyev, Alexander P. et al. / Synthesis, structure and optical properties of the laser synthesized Al2O3 nanopowders depending on the crystallite size and vaporization atmosphere. In: Advanced Powder Technology. 2021 ; Vol. 32, No. 8. pp. 2733-2742.

BibTeX

@article{7cebedf894c3419885df8171e4ed2729,
title = "Synthesis, structure and optical properties of the laser synthesized Al2O3 nanopowders depending on the crystallite size and vaporization atmosphere",
abstract = "A series of Al2O3 nanoparticles with the sizes ranging from ~ 2 to 21 nm, according to XRD, HRTEM and BET, was obtained by vaporization of α-Al2O3 in flowing helium and argon at different pressures under the action of a cw CO2 laser. The particle size was changed by varying the composition of ambient gas (He, Ar) and its pressure in a vaporization chamber from 0.034 to 0.9 bar. The effect of the synthesis conditions on the properties of Al2O3 nanopowders is presented and discussed. Particles with the size smaller than 6–7 nm have a faceted shape, whereas the shape of larger particles is close to spherical. It was found that the resulting nanopowders consist of a mixture of transition aluminas, among which the γ-polymorph is dominant. Thermal analysis showed that for smaller nanoparticles the phase transition to α-Al2O3 occurs at a lower temperature. In nominally pure Al2O3 nanoparticles with different sizes, photoluminescence at RT and 80 K is determined by trace level concentrations (≤10–3 wt%) of uncontrolled impurities of 3d elements (Cr3+(Oh) and Fe3+(Td)), surface hydroxyl groups, and point defects represented mostly by F-type centers. The acquired experimental data indicate that manifestation of the size effect for Al2O3 nanoparticles has a boundary corresponding to 6–7 nm. Al2O3 nanoparticles with the dominant γ-Al2O3 structure obtained by the laser method can be promising in many chemical reactions, particularly as the supports of catalysts and sorbents, for which the high specific surface area is of special importance.",
keywords = "3d elements, AlO nanoparticles, F-centers, Hydroxyl groups, Laser vaporization, Physical vapor deposition, Size effect",
author = "Kostyukov, {Anton I.} and Snytnikov, {Valeriy N.} and Yelisseyev, {Alexander P.} and Zhuzhgov, {Aleksey V.} and Kostyukova, {Nadezhda Y.} and Ishchenko, {Arcady V.} and Cherepanova, {Svetlana V.} and Snytnikov, {Valeriy N.}",
note = "Funding Information: The study was supported by the Russian Foundation for Basic Research within project No. 19-32-60027 and partially supported by the Ministry of Science and Higher Education of the Russian Federation within the governmental order for Boreskov Institute of Catalysis (project AAAA-A21-121011390009-1 ). Publisher Copyright: {\textcopyright} 2021 The Society of Powder Technology Japan Copyright: Copyright 2021 Elsevier B.V., All rights reserved.",
year = "2021",
month = aug,
doi = "10.1016/j.apt.2021.05.044",
language = "English",
volume = "32",
pages = "2733--2742",
journal = "Advanced Powder Technology",
issn = "0921-8831",
publisher = "Elsevier",
number = "8",

}

RIS

TY - JOUR

T1 - Synthesis, structure and optical properties of the laser synthesized Al2O3 nanopowders depending on the crystallite size and vaporization atmosphere

AU - Kostyukov, Anton I.

AU - Snytnikov, Valeriy N.

AU - Yelisseyev, Alexander P.

AU - Zhuzhgov, Aleksey V.

AU - Kostyukova, Nadezhda Y.

AU - Ishchenko, Arcady V.

AU - Cherepanova, Svetlana V.

AU - Snytnikov, Valeriy N.

N1 - Funding Information: The study was supported by the Russian Foundation for Basic Research within project No. 19-32-60027 and partially supported by the Ministry of Science and Higher Education of the Russian Federation within the governmental order for Boreskov Institute of Catalysis (project AAAA-A21-121011390009-1 ). Publisher Copyright: © 2021 The Society of Powder Technology Japan Copyright: Copyright 2021 Elsevier B.V., All rights reserved.

PY - 2021/8

Y1 - 2021/8

N2 - A series of Al2O3 nanoparticles with the sizes ranging from ~ 2 to 21 nm, according to XRD, HRTEM and BET, was obtained by vaporization of α-Al2O3 in flowing helium and argon at different pressures under the action of a cw CO2 laser. The particle size was changed by varying the composition of ambient gas (He, Ar) and its pressure in a vaporization chamber from 0.034 to 0.9 bar. The effect of the synthesis conditions on the properties of Al2O3 nanopowders is presented and discussed. Particles with the size smaller than 6–7 nm have a faceted shape, whereas the shape of larger particles is close to spherical. It was found that the resulting nanopowders consist of a mixture of transition aluminas, among which the γ-polymorph is dominant. Thermal analysis showed that for smaller nanoparticles the phase transition to α-Al2O3 occurs at a lower temperature. In nominally pure Al2O3 nanoparticles with different sizes, photoluminescence at RT and 80 K is determined by trace level concentrations (≤10–3 wt%) of uncontrolled impurities of 3d elements (Cr3+(Oh) and Fe3+(Td)), surface hydroxyl groups, and point defects represented mostly by F-type centers. The acquired experimental data indicate that manifestation of the size effect for Al2O3 nanoparticles has a boundary corresponding to 6–7 nm. Al2O3 nanoparticles with the dominant γ-Al2O3 structure obtained by the laser method can be promising in many chemical reactions, particularly as the supports of catalysts and sorbents, for which the high specific surface area is of special importance.

AB - A series of Al2O3 nanoparticles with the sizes ranging from ~ 2 to 21 nm, according to XRD, HRTEM and BET, was obtained by vaporization of α-Al2O3 in flowing helium and argon at different pressures under the action of a cw CO2 laser. The particle size was changed by varying the composition of ambient gas (He, Ar) and its pressure in a vaporization chamber from 0.034 to 0.9 bar. The effect of the synthesis conditions on the properties of Al2O3 nanopowders is presented and discussed. Particles with the size smaller than 6–7 nm have a faceted shape, whereas the shape of larger particles is close to spherical. It was found that the resulting nanopowders consist of a mixture of transition aluminas, among which the γ-polymorph is dominant. Thermal analysis showed that for smaller nanoparticles the phase transition to α-Al2O3 occurs at a lower temperature. In nominally pure Al2O3 nanoparticles with different sizes, photoluminescence at RT and 80 K is determined by trace level concentrations (≤10–3 wt%) of uncontrolled impurities of 3d elements (Cr3+(Oh) and Fe3+(Td)), surface hydroxyl groups, and point defects represented mostly by F-type centers. The acquired experimental data indicate that manifestation of the size effect for Al2O3 nanoparticles has a boundary corresponding to 6–7 nm. Al2O3 nanoparticles with the dominant γ-Al2O3 structure obtained by the laser method can be promising in many chemical reactions, particularly as the supports of catalysts and sorbents, for which the high specific surface area is of special importance.

KW - 3d elements

KW - AlO nanoparticles

KW - F-centers

KW - Hydroxyl groups

KW - Laser vaporization

KW - Physical vapor deposition

KW - Size effect

UR - http://www.scopus.com/inward/record.url?scp=85108721999&partnerID=8YFLogxK

U2 - 10.1016/j.apt.2021.05.044

DO - 10.1016/j.apt.2021.05.044

M3 - Article

AN - SCOPUS:85108721999

VL - 32

SP - 2733

EP - 2742

JO - Advanced Powder Technology

JF - Advanced Powder Technology

SN - 0921-8831

IS - 8

ER -

ID: 28867222